PA6 Ultramid® 8202 L 德国巴斯夫
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
物性表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
|---|---|---|---|---|
| 吸水率 | 平衡,50%RH | ASTM D570 | 2.7 | % |
| 饱和 | ASTM D570 | 9.5 | % | |
| 24hr | ASTM D570 | 1.6 | % | |
| 收缩率 | MD：3.18mm | - | 1.2 | % |
| 密度 | - | ASTM D792 | 1.13 | g/cm³ |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 拉伸强度 | 屈服,-40°C | ASTM D638 | 125 | MPa |
| 弯曲模量 | 121°C | ASTM D790 | 305 | MPa |
| 90°C | ASTM D790 | 350 | MPa | |
| 65°C | ASTM D790 | 500 | MPa | |
| 23°C | ASTM D790 | 2830 | MPa | |
| -40°C | ASTM D790 | 3010 | MPa | |
| 伸长率 | 断裂,23°C | ASTM D638 | 55 | % |
| Yield,121°C | ASTM D638 | 36 | % | |
| 屈服,80°C | ASTM D638 | 42 | % | |
| 屈服,23°C | ASTM D638 | 4.0 | % | |
| 拉伸强度 | 断裂,23°C | ASTM D638 | 75.0 | MPa |
| 弯曲强度 | 121°C | ASTM D790 | 20.0 | MPa |
| 90°C | ASTM D790 | 20.0 | MPa | |
| 65°C | ASTM D790 | 30.0 | MPa | |
| 拉伸强度 | 屈服,23°C | ASTM D638 | 79.0 | MPa |
| 屈服,80°C | ASTM D638 | 35.0 | MPa | |
| Yield,121°C | ASTM D638 | 25.0 | MPa | |
| 弯曲强度 | -40°C | ASTM D790 | 170 | MPa |
| 23°C | ASTM D790 | 110 | MPa | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 线性热膨胀系数 | MD | ASTME831 | 8.3E-05 | cm/cm/°C |
| 熔融温度 | - | ASTM D3418 | 220 | °C |
| 热变形温度 | 1.8MPa,未退火 | ASTM D648 | 65.0 | °C |
| 0.45MPa,未退火 | ASTM D648 | 178 | °C | |
| 硬度 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 洛氏硬度 | R级 | ASTM D785 | 119 | - |
| 冲击性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 悬臂梁缺口冲击强度 | 23°C | ASTM D256 | 60 | J/m |
| -40°C | ASTM D256 | 50 | J/m |